Heavy-Duty Anti-Corrosion

Highly efficient general-purpose anti-rust protective material. Designed for rapid engineering, it requires no complex multi-layer application. A single coat tightly adheres to metal substrates, effectively blocking moisture, salt fog, and chemical corrosive agents.

• Steel Adhesion: 4B Highest Grade (ASTM D3359)
• Salt Spray Resistance: ≥ 1000 hours with no blistering/peeling
• Recommended DFT: Dry Film Thickness 60-80 μm

Features outstanding weather resistance, color retention, and UV resistance. The coating film is full, wear-resistant, and chemically stable. Frequently used as the topcoat in anti-corrosion systems to maintain aesthetics and long-term protection.

• Accelerated Weathering: QUV test ≥ 2000 hours
• Gloss Retention: ≥ 85%, absolutely no fading/chalking
• Wear Resistance: Meets heavy industrial protection standards

Heat-resistant anti-corrosion coating explicitly designed for high-temperature environments. Will not crack or peel under high heat. Widely applied on petrochemical pipelines, exhaust pipes, and boiler exterior walls subjected to thermal cycling.

• Temperature Resistance: Continuous 400°C / Intermittent 500°C
• Thermal Shock Resistance: No peeling after 10 cold-hot cycles
• Applicable Substrates: Carbon steel, stainless steel, and various alloys

High-content zinc-rich anti-rust primer providing top-tier electrochemical cathodic protection for steel substrates. Offers excellent chemical resistance and weldability. The premier choice for heavy anti-corrosion of large petrochemical steel structures and bridges.

• Dry Film Zinc Content: Meets heavy anti-corrosion standards (≥ 80%)
• Cathodic Protection: Outstanding electrochemical defense at cut edges
• Application Adaptability: Excellent fast drying and weldability

Impact-resistant anti-rust coating featuring excellent adhesion, water resistance, alkali resistance, and solvent resistance. Forms a tough film upon curing, effectively defending against acid/alkali gases and harsh chemical environments.

• Adhesion Strength: 5B Highest Grade (ASTM D3359)
• Chemical Resistance: Resists 10% sulfuric acid & sodium hydroxide
• Overcoating Interval: Minimum 4 hours (at 25°C environment)

Anti-rust coating rich in Micaceous Iron Oxide (MIO). The flake-like MIO crystals overlap after curing to form a labyrinth-like barrier, physically isolating moisture and salt penetration. Delivers high-strength physical shielding protection.

• MIO Flake Content: Significant physical shielding effect (≥ 35%)
• Labyrinth Effect: Strongly blocks water molecules and chloride ions
• System Compatibility: As an intermediate coat, provides excellent intercoat adhesion